intergranular stress corrosion

基本解释

The exfoliation of alloy happens from original pitting to intergranular corrosion and with cooperation of stress.
研究表明，合金的剥蚀是一个从点蚀发展到晶间腐蚀，然后在应力协同作用下发生破坏的过程。
The cracking of alloy with very low stress-corrosion resistance, welded and stored in open air for a long time, is caused by the welded stress and such a fracture is a typical intergranular fracture.
抗应力腐蚀性能低的合金焊接后，在大气中长期存放沿熔合线发生的开裂，是由焊接应力引起的，断口是典型的脆性沿晶断裂。
The corrosion behavior of 2D12 alloy was evaluated including intergranular corrosion, exfoliation and stress corrosion cracking.
对不同规格2D12铝合金进行晶间腐蚀、剥蚀和应力腐蚀性能测定。