基本解释

Residual MgO-CaO brick after being used in AOD furnace was determined by OM, SEM and EDAX. Corrosion mechanism of MgO-CaO brick as furnace lining was studied.
采用光学显微镜（OM）、扫描电镜（SEM）和能谱仪（E DAX）对AOD炉用镁钙砖的残砖进行了分析，探讨了炉衬镁钙砖的侵蚀机理。
The high-power electric are furnace lining burnt and damaged are analyzed in the paper, and puts forward some measures to prolong the furnace lining durability.
本文分析了高功率电弧炉炉壁烧损的原因，提出了提高炉衬寿命的措施。
The hot and wet sprayed material has excellent air permeability, and may be sprayed to the surface of metallurgical furnace lining at 800-900 deg c without producing crack.
本发明的湿式喷射料具有良好的透气性，可对800～900 ℃高温下的冶金炉衬表面进行喷射而不产生爆裂现象。