breaking elongation rate

基本解释

The properties including bulging rate, breaking elongation rate and breaking strength of the jute fiber were tested under the different conditions.
分别测定了不同工艺条件下黄麻纤维的膨化率、断裂伸长率、断裂强力的变化。
The constant creep rate and creep breaking elongation were increased and creep-resistance breaking time was decreased with the increase of room temperature.
随环境温度的升高，纤维的恒蠕变速率增大，抗蠕变断裂时间变小，蠕变断裂伸长变大；
Tests on film tension strength, elongation rate at breaking, anti carbonation effect etc. and applied technique of elastomeric latex coating for exterior wall are described.
介绍了涂膜拉伸强度、断裂时的延伸率，防碳化效应特性试验以及弹性外墙乳胶涂料施工应用技术。

断裂伸长率
The tensile strength of the film was 34.82 MPa, and the breaking elongation rate was 331%, which reach for the national standard GB4456-84.8.
膜的拉伸强度可达34.82MPa，断裂伸长率为331%，达到国标GB4456一84所规定的标准。